5litres – £148.15
ALLCOAT Chemical Resistant Coating is a high grade, 2 pack, hard wearing epoxy floor coating designed for maximum chemical resistance which is also light, fast and flexible. It is ideal where a seamless finish is required. ALLCOAT Chemical Resistant Coating has good resistance to impact abrasion and trafficking. The system is resistant to high temperatures up to 150°C. Slight discolouration may occur at extreme temperatures.
Features & Benefits
- Maximum chemical resistance
- Rapid set properties – touch dry in just 5 hours
- Good abrasion and impact resistance
- Easy cleaning, including removal of graffiti
- Light and fast installation – usually just one coat required
- Resistant to thermal shock & hot water
- Hygienic – does not support fungus or bacterial growth
- Attractive range of colours available
- Food preparation and manufacturing areas
- Chemical plants
- Aircraft hangers
- Vehicle maintenance bays
- Operating theatres
- Any areas where a long lasting, easily cleaned, high chemical resistance finish is essential
Concrete shall be a minimum of 21 days old and/or the residual moisture content shall be below 6%. Ensure that the concrete is clean and free from dust, laitance, oil, curing compound, existing paint finishes, etc. Blow holes and defective concrete shall be made good using a proprietary repair compound e.g. ALLCOAT Epoxy Repair Mortar. Suitable mechanical treatment, such as vacuum grit-blasting, is the preferred treatment prior to application, as this ensures a mechanical key for the coating.
Steel surfaces shall be shot blasted or grit blasted to a nominal Sa 2.5 Swedish standard. All dust and grease shall be removed prior to coating application. If a delay is likely to occur between blasting and application then it is recommended that a coat of ALLCOAT QD Primer be applied as holding primer to obviate flash rusting.
Apply onto the properly prepared surface a coat of ALLCOAT WB Primer for porous surfaces.
Mixing & Application
Pour the contents of the CURING AGENT tin into the BASE container and thoroughly mix, preferably by mechanical means until a uniform colour is achieved.
Apply by brush, short piled roller or airless spray at a nominal rate of 0.3 – 0.5 kg/m²/coat, depending on overall dry film thickness required. After a minimum of 14 hours @ 20°C, but within a maximum of 48 hours, apply a second coat at the same nominal rate. If the maximum over-coating limit is exceeded, the first coat must be abraded and solvent wiped prior to application of the second coat. Should a slip resistant finish be required, then a broadcast of graded Silica Sand, or Silicon Carbide shall be made immediately after the first coat. Brush off excess aggregate prior to application of the second coat.
Blue, Dark Grey, Mid Green, Mid Grey, Tile Red
5m² per L per coat
|Dry film thickness||
125 microns at a coverage rate of 8m² per L
40 minutes at 20°C
|Touch dry time||
5 hours at 20°C
|Full Cured Time||
Allow to cure for a minimum of 14 hours @ 20°C prior to light foot trafficking, and 24 hours @ 20°C prior to vehicular trafficking. Allow a minimum of 5 days cure @ 20°C for optimum chemical resistance.
|Full chemical resistance||
5 days at 20°C. Excellent chemical resistance to all acids, solvents and alkalis.
2 years at ambient temperature